PTFE coated glass cloth in black color is always with anti-static property, ideal for fusing process
PTFE coated glass cloth anti-static is specially treated fabric with adding fillers to dissipate static build up, in the meantime, remain all the properties of common PTFE fiberglass fabric such as optimal quick release surface, high temperature resistant, chemical resistant, abrasion resistant and non-flammable. 
Mutiflon provide anti-static PTFE coated glass cloth in different thickness such as 0.08mm, 0.13mm, 0.25mm, 0.35mm and 0.38mm. 0.08mm and 0.13mm material is normally used as release sheet or gasket in electric industry, 0.25mm, 0.35mm and 0.38mm material is suitable for making into conveyor belts for fusing machines.
10mil anti static PTFE coated fiberglass cloth is common to make into conveyor belts for fusing press machine, the material surface will eliminate static electricity, perfect for clothing and textile industry. We also provide extra wide anti static PTFE coated glass cloth up to 2600mm, with smooth and glossy surface. Our code for this material is MT9025BJ 
Data Sheet for MT9025BJ
| Product | Product Category | Coating Material |
PTFE FIBERGLASS | ANTI-STATIC | PTFE |
FEATURES | METRIC | IMPERIAL |
Standard Width | 1000mm, 1250mm, 1500mm, 2000mm, 2600mm | 39inches, 49inches, 59inches, 78.7inches, 102.3inches |
Thickness | 0.25mm | 0.010inches |
Coated Weight | 530g/m2 | 15.63 oz/sq yd |
PTFE Content | 62% | 62% |
Tensile Strength | 460 N/cm Warp | 263 lbs/inches Warp |
400 N/cm Weft | 229 lbs/inches Weft | |
Temperature Resistance | -73-260℃ | -100-500℉ |
How to joint the PTFE Coated Fiberglass Cloth
First, cut the material into required belt size with two ends in angle, put two ends overlap together with a piece of FEP film in the middle(the overlap part can be 25mm, 40mm, 50mm according to belt size),set the handle iron machine to 400℃ and use it to press the joint part. 
Heat sealer
FEP film